ASTM A519 Grade 1026 Carbon Steel Seamless Tubings are Medium Carbon Steel Tubings with 0.22-0.28 % carbon content with combination of 0.60-0.90 % manganese. These Tubings are most commonly used for general purpose applications worldwide. ASTM A519 Grade 1026 Tubings are ductile and strong Tubings with long wearing properties. These Tubings are manufactured as per ASTM Specification and commercially referred as carbon steel Tubings.
ASTM A519 covers several grades of carbon and alloy steel seamless mechanical tubing.
ASTM A519 covers both seamless hot-finished mechanical tubing and seamless cold-finished mechanical tubing in sizes up to and including 12 3⁄4 in. (323.8 mm) outside diameter for round tubes with wall thicknesses as required.
Standard: ASTM A519 / ASME SA 519.
Description Name: ASME SA 519 / ASTM A519 GR.1026 boiler pipes, A519 pipes, Grade 1026 ASTM A519 carbon steel tube, ASTM A519 GR. 1026 mechanical pipes, ASTM A 519 GR.1026 carbon steel pipe, Grade 1026 SEAMLESS PIPE, ASTM A519 Grade 1026 cold drawn seamless steel tubes, ASTM A519 Gr.1026 pipes and tubing, ASTM A519 SAE1026 seamless tubing, alloy steel tube, carbon steel tube, mechanical tubing, Seamless steel tube, steel tube.
- Size: 6mm-323.8mm.
- Schedule: 10-XXS / Thk.
- Shape: Round or Special sections.
- Length: Single random length/ Double random length or as customer’s actual request.
- Grade: SAE 1026 / AISI 1026 / GRADE 1026.
Condition: The purchaser shall specify a sizing method and, if required, a thermal treatment.
Chemical component
| Grade | C | Mn | P≤ | S≤ |
| 1026 | 0.22-0.28 | 0.60-0.90 | 0.040 | 0.050 |
Mechanical properties
| Properties | Metric | Imperial |
| Tensile strength | 490 MPa | 71100 psi |
| Yield strength | 415 MPa | 60200 psi |
| Bulk modulus (typical for steel) | 140 GPa | 20300 ksi |
| Shear modulus (typical for steel) | 80.0 GPa | 11600 ksi |
| Elastic modulus | 190-210 GPa | 27557-30458 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (In 50 mm) | 15.00% | 15.00% |
| Reduction of area | 40.00% | 40.00% |
| Hardness, Brinell | 143 | 143 |
| Hardness, Knoop (converted from Brinell hardness) | 163 | 163 |
| Hardness, Rockwell B (converted from Brinell hardness) | 78 | 78 |
| Hardness, Vickers (converted from Brinell hardness) | 149 | 149 |
Mechanical Test Requirements:
Hardness Test, Tension Tests, Nondestructive tests, Steel Cleanliness, Hardenability, Flaring Test
ASTM A519-89/ASME SA519 Material comparison tables
Seamless mechanical tubing is manufactured from carbon and alloy steels for structural or other mechanical purposes involving machining or heat treating, where close tolerances, smooth finish, or definite physical properties are important factors.
Scope
1.1 this specification covers several frades of carbon and alloy steel seamless mechanical tubing. The frades anr listed in Tables 1, 2, and 3. When welding is used for joining the weldable mechanical tube grades, the welding procedure shall be suitable for the frade, the condition of the components, and the intended service.
1.2 This specification covers both seamless hot-finished emchanical tubing and seamless cold-finished mechanical tubing in sizes up to and including 12 3/4 in.(322.8mm) outside diameter of rround tubes with wall thicknesses as required.
1.3 The tubes shall be furnished in the following shapes, as specified by the purchaser:round, square, rectagular, and special sections.
1.4 Supplementary requirements of an optional nature are provided and when desired shall be so stated in the order.