ASTM A333 specification describes Low temperature service pipe applied up to minus 150 degrees Fahrenheit. These pipe are always provided in normalized condition with Charpy Impact V-Notch Test as per the temperature range requirements to assure compatibility with the applicable environments.
Low temperature pipe also known as LTCS pipe abbreviated as LOW TEMPERATURE CARBON STEEL pipe. Since heavier wall thickness has an adverse effect on the low temperature impact properties, the size availability is limited in this specification.
Several grades of ferritic steel are included. Some product sizes may not be available under this specification because heavier wall thicknesses have an adverse effect on low-temperature impact properties.
A333 pipe is furnished to nine different grades designated by numbers 1, 3, 4, 6, 7, 8, 9, 10, & 11.
Sunny Steel Supply supplies a full range of ASTM A333 (ASME S/A 333)
Low Temperature Steel Pipe Specifications & Grades
- SA333 & A333 – Grades 1, 3, 6 & 8
- A671 CC65 CL22 EFW at -50°F (Welded Alternative to A333)
- Flanges: A/SA 350 LF2, LF3
- Fittings: A/SA-420 WPL6, WPL3
Size range
- 1/4” Nominal to 24”O.D.
- Schedules: STD, 40, XH, 60, 80, 100, 120, 140, 160, XXH
- Unscheduled heavy wall pipe thicknesses available up to 4 inches.
For low temperature
Production specification range of low temperature pipe products
Pipes are used in low temperature service
Steel pipes are produced accord to ASTM A333 standard
Strike temperature condition：
| Crade | The lowest temperature for strike test | |
| ℉ | ℃ | |
| ASTM A333 Grade 1 | -50 | -45 |
| ASTM A333 Grade 6 | -50 | -45 |
Mechanical requiremnts of ASTM A333 alloy pipe
| Grade | Tensile Strength (MPa） | Yield Point (MPa) | Elongation (%) | |
| Y | X | |||
| Grade 1 | ≥380 | ≥205 | ≥35 | ≥25 |
| Grade 3 | ≥450 | ≥240 | ≥30 | ≥20 |
| Grade 4 | ≥415 | ≥240 | ≥30 | ≥16.5 |
| Grade 6 | ≥415 | ≥240 | ≥30 | ≥16.5 |
| Grade 7 | ≥450 | ≥240 | ≥30 | ≥22 |
| Grade 8 | ≥690 | ≥515 | ≥22 | |
| Grade 9 | ≥435 | ≥315 | ≥28 | |
| Grade 10 | ≥550 | ≥450 | ≥22 | |
| Grade 11 | ≥450 | ≥240 | ≥18 | |
Chemical Composition (%) of ASTM A333 steel pipe
| Grade | Chemical Composition (%) | ||||||||||
| C | Si | Mn | P | S | Cr | Ni | Cu | Mo | V | Al | |
| Grade 1 | ≤0.30 | 0.40-1.06 | ≤0.025 | ≤0.025 | |||||||
| Grade 3 | ≤0.19 | 0.18-0.37 | 0.31-0.64 | ≤0.025 | ≤0.025 | 3.18-3.82 | |||||
| Grade 4 | ≤0.12 | 0.18-0.37 | 0.50-1.05 | ≤0.025 | ≤0.025 | 0.44-1.01 | 0.47-0.98 | 0.40-0.75 | 0.04-0.30 | ||
| Grade 6 | ≤0.30 | ≥0.10 | 0.29-1.06 | ≤0.025 | ≤0.025 | ||||||
| Grade 7 | ≤0.19 | 0.13-0.32 | ≤0.90 | ≤0.025 | ≤0.025 | 2.03-2.57 | |||||
| Grade 8 | ≤0.13 | 0.13-0.32 | ≤0.90 | ≤0.025 | ≤0.025 | 8.40-9.60 | |||||
| Grade 9 | ≤0.20 | 0.40-1.06 | ≤0.025 | ≤0.025 | 1.60-2.24 | 0.75-1.25 | |||||
| Grade 10 | ≤0.20 | 0.10-0.35 | 1.15-1.50 | ≤0.03 | ≤0.015 | ≤0.15 | ≤0.25 | ≤0.015 | ≤0.50 | ≤0.12 | ≤0.06 |
| Grade 11 | ≤0.10 | ≤0.35 | ≤0.6 | ≤0.025 | ≤0.025 | ≤0.50 | 35.0-37.0 | ≤0.50 | |||
Heat Treatment:
Grades 1 and 6 shall be heat treated to control their microstructure.
ASTM A333 Grade 6 and ASME SA 333 Grade 6 are heat treated to achieve normalized condition @ 920 degrees Celsius with controlled microstructure.
Production specification range of low temperature pipe products
Specific Impact requirements
The raw material used for low temperature service pipe is ALUMINIUM killed with high proportion of manganese (more than 1%) combined with low proportions of carbon (less than 0.23%).For low temperature pipe to be certified as LTCS additional impact test should be conducted at low temperatures, as per mandatory requirements in section 8 of ASTM A 333.