16Mn steel pipe

The range of 16Mn pipe sizes that may be examined by each method shall be subjected to the limitations in the scope of the respective practice.

16Mn is a kind of high strength low alloy structural steel, the carbon content of 0.12% -0.20% to join main alloying elements manganese, silicon, vanadium, niobium, and titanium.

16Mn seamless tubes for high pressure boiler 16Mn Steel is a carbon-manganese steel, carbon content of 0.16%, the yield point is equal to 343MPa (strength level belonging to 343MPa). 

Less the 16Mn steel alloy content, good weldability, and generally do not have to warm-up before welding.

Mechnical property for Q345B low alloy structural steel:



The main chemical compositions(%) of 16Mn:

ElementsData
Carbon0.12-0.20
Silicon0.20-0.60
Manganese1.20-1.60
Chromium
Molybdenum

Mechanical Properties of 16Mn:

PropertiesData
Tesile ób/Mpa470-660
Yield ós/Mpa(min)275-345
Elongation δ5(%)(min)21
SAFA Aku/J(min)-
Brinel hardness HBS(max)-

The W.T. tolerance of 16Mn:

W.T.(S)Tolerance of W.T.
<3.5 +15%(+0.48mm min)
 -10%(+0.32mm min)
3.5-20+15%,-10%
>20D<219±10%
D≥219+12.5%,-10%



Comments

Hot products

ASTM A335 Chrome Moly Pipe

Steel pipe world standards

ASTM A333 Grade 6 Seamless Pipe

ASTM A106 Seamless carbon steel tube for high temperature service

Orifice Flanges

ASTM A213 T22 alloy tube

API Spec 5CT - Specification for Casing and Tubing

Tubing, Casing and Line Pipes

Seamless Steel Pipe and Tubes

ASTM A335 P22 alloy steel pipe

Labels

Show more

Hot products

Bimetal Clad Pipe

Bimetal Clad Pipe
Bimetal Clad Pipe is cast with mold vanishing vacuum suction casting cladding process.

Contact us

Name

Email *

Message *